IXPE (irradiation cross-linked polyethylene) foam is based on low density polyethylene as raw material, change to independent obturator meshed bubble structure by using electronic irradiation. It is a kind of continues foaming freely, smooth surface, closed-cell, independent, well-distributed, no water absorption, unlimited length and adjustable color and density soft foaming material. Compare with other similar foaming materials, the performance of IXPE is more excellent. Especially for environmental protection, sound insulation, water proof, moisture proof, shock absorption, cushioning, flexible, heat preservation, heat insulation, weatherability, aging resistant and lightweight.IXPE can be compounded with PE film; colorful film and aluminum foil which are used in automotive trim or heat insulation in home air-conditioning or central air-conditioning system.Widely used in flooring underlayment. It is one of the most environmental protection, best sound insulation and moisture resistant product in flooring underlay.
| IXPE foam specification | ||||||||||||
| Test Item | Index | Standards | ||||||||||
| 3Times | 5Times | 8Times | 10Times | 15Times | 20Times | 25Times | 30Times | 35Times | 40Times | |||
| Density （kg/m3） | 300±40 | 200±30 | 125±15 | 100±10 | 66.7±8 | 50±6 | 40±4 | 33.3±3 | 28.6±3 | 26±3 | GB/T6343 | |
| Shore Hardnes （°） | Thick＞3mm | 65～75 | 60～70 | 50～60 | 45～50 | 35～45 | 30～35 | 25～30 | 18～25 | 13～18 | 13～18 | GB/T2411 |
| Thick≤3mm | 55～65 | 45～55 | 35～45 | 25～35 | 20～25 | 15～20 | ||||||
| Tensile Stength （Mpa） | T | ≥1.4 | ≥1.3 | ≥0.9 | ≥0.7 | ≥0.5 | ≥0.4 | ≥0.3 | ≥0.2 | ≥0.15 | ≥0.15 | GB/T6344 |
| L | ≥1.6 | ≥1.5 | ≥1.0 | ≥0.8 | ≥0.6 | ≥0.5 | ≥0.4 | ≥0.25 | ≥0.2 | ≥0.2 | ||
| Elongation (%) | T | ≥210 | ≥200 | ≥150 | ≥130 | ≥130 | ≥130 | ≥110 | ≥110 | ≥100 | ≥100 | GB/T6344 |
| L | ≥230 | ≥220 | ≥170 | ≥150 | ≥150 | ≥150 | ≥120 | ≥120 | ≥110 | ≥110 | ||
| Tearing Stength (KN/m) | T | ≥10 | ≥9 | ≥8 | ≥6 | ≥4 | ≥2.5 | ≥2 | ≥1.5 | ≥1.3 | ≥1.3 | GB/T10808 |
| L | ≥10 | ≥9 | ≥8 | ≥6 | ≥4 | ≥2.5 | ≥2 | ≥1.2 | ≥1.2 | ≥1.2 | ||
| Compressed Distortions （%）23℃±2℃，22h | ≤2 | ≤2 | ≤3 | ≤5 | ≤7 | ≤8 | ≤9 | ≤10 | ≤11 | ≤11 | GB/T6669 | |
| Size change rate （%）70±2℃，22h | T | ≤-4 | ≤-4 | ≤-4 | ≤-4 | ≤-4 | ≤-6 | ≤-6 | ≤-6 | ≤-6 | ≤-6 | GB/T8811 |
| L | ≤-6 | ≤-6 | ≤-6 | ≤-6 | ≤-6 | ≤-8 | ≤-8 | ≤-8 | ≤-8 | ≤-8 | ||
| Water Absorbtion (g/cm2)23℃±2℃，24h | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.03 | ≤0.03 | ≤0.04 | ≤0.04 | ≤0.05 | ≤0.05 | ≤0.05 | GB/T1034 | |
| Thermal Conductivity （w/m.k） | ≤0.095 | ≤0.095 | ≤0.084 | ≤0.073 | ≤0.065 | ≤0.055 | ≤0.049 | ≤0.045 | ≤0.040 | ≤0.040 | GB/T10297 | |