XPE is a chemical crosslinked polyethylene foam, with low density polyethylene resin and a crosslinking agent and foaming agent through continuous foaming and high temperature, XPE is chemically stable, difficult to decompose, odorless and flexible. It is the preferred material for making mat, soundproof layer, heat insulation layer and automobile foot pad.
| CYG TEFA CO.,LTD | ||||||||||||
| XPE foam specification | ||||||||||||
| Test Item | Index | Standards | ||||||||||
| 3Times | 5Times | 8Times | 10Times | 15Times | 20Times | 25Times | 30Times | 35Times | 40Times | |||
| Density （kg/m3） | 300±40 | 200±30 | 125±15 | 100±10 | 66.7±8 | 50±6 | 40±4 | 33.3±3 | 28.6±3 | 26±3 | GB/T6343 | |
| Shore Hardnes （°） | 65～75 | 60～70 | 50～60 | 45～50 | 35～45 | 30～35 | 25～30 | 18～25 | 13～18 | 13～18 | GB/T2411 | |
| Tensile Stength(Mpa） | T | ≥1.4 | ≥1.3 | ≥0.9 | ≥0.7 | ≥0.5 | ≥0.35 | ≥0.3 | ≥0.2 | ≥0.15 | ≥0.15 | GB/T6344 |
| L | ≥1.6 | ≥1.5 | ≥1.0 | ≥0.8 | ≥0.6 | ≥0.38 | ≥0.35 | ≥0.25 | ≥0.2 | ≥0.2 | ||
| Elongation (%) | T | ≥150 | ≥130 | ≥125 | ≥110 | ≥100 | ≥80 | ≥80 | ≥80 | ≥70 | ≥70 | GB/T6344 |
| L | ≥170 | ≥150 | ≥125 | ≥120 | ≥110 | ≥90 | ≥90 | ≥90 | ≥80 | ≥80 | ||
| Tearing Stength (KN/m) | T | ≥11 | ≥9 | ≥8 | ≥6 | ≥4 | ≥2.5 | ≥2 | ≥1.5 | ≥1.3 | ≥1.3 | GB/T10808 |
| L | ≥11 | ≥9 | ≥8 | ≥6 | ≥4 | ≥2.5 | ≥2 | ≥1.2 | ≥1.2 | ≥1.2 | ||
| Compressed Distortions （%）23℃±2℃，22h | ≤2 | ≤2 | ≤3 | ≤5 | ≤7 | ≤8 | ≤9 | ≤10 | ≤11 | ≤11 | GB/T6669 | |
| Size change rate （%）70±2℃，22h | T | ≤-4 | ≤-4 | ≤-4 | ≤-4 | ≤-4 | ≤-6 | ≤-6 | ≤-6 | ≤-6 | ≤-6 | GB/T8811 |
| L | ≤-6 | ≤-6 | ≤-6 | ≤-6 | ≤-6 | ≤-8 | ≤-8 | ≤-8 | ≤-8 | ≤-8 | ||
| Water Absorbtion (g/cm2)23℃±2℃，24h | ≤0.02 | ≤0.02 | ≤0.02 | ≤0.03 | ≤0.03 | ≤0.04 | ≤0.04 | ≤0.05 | ≤0.05 | ≤0.05 | GB/T1034 | |
| Thermal Conductivity （w/m.k） | ≤0.095 | ≤0.095 | ≤0.084 | ≤0.073 | ≤0.065 | ≤0.055 | ≤0.049 | ≤0.045 | ≤0.040 | ≤0.040 | GB/T10297 | |