Product Details:
|
Density: | 25-333 Kg/m3 | Thickness: | 0.1-100mm |
---|---|---|---|
Material: | LDPE | Type: | Other Heat Insulation Materials,air Conditioner |
Flammability: | B1,class 1 | Length: | 6-12m Or Custom |
Highlight: | thermal insulation materials,fireproof xpe foam |
Fire Proof Expanded Polyethylene Sheet Insulation PE XPE IXPE Foam
Electronic cross-linked polyethylene foam also named Physical crosslinked polyethyele foam, Irradiation crosslinked polyethylene foam.Common abbreviations IXPE foam, IXLPE foam.It is made of low-density polyethylene (LDPE), AC foaming agent and other powders after being melted, mixed and extruded, and then foamed at high temperature. IXPE has finer cells, smoother surface and better mechanical properties than XPE.
Production process: compounding-extrusion-irradiation-foaming.
Note: IXPE foam can be made anti-static (we will talk about anti-static IXPE later), but XPE cannot (theoretically it is possible, but our company does not currently produce).
Specifications
|
||||
Property | Standard | Unit | Value | |
Density | - | Kg/m³ | 28.00 | |
Tensile Strength | Transverse | ISO-1798 | MPa | 0.33~0.35 |
Longitudinal | 0.35~0.41 | |||
Tearing Strength | Transverse |
ISO-8067
|
Kn/m | 1.52~1.60 |
Longitudinal | 1.94~2.00 | |||
Compression 25% | ISO-3386-1 | kPa | 29.60 | |
Compression 45% | ISO-3386-1 | kPa | 54.40 | |
Compression 50% | ISO-3386-1 | kPa | 79.50 | |
Compression Set 25% 0.5H | ISO-1856 | % | 16.50 | |
Compression Set 25% 24H | ISO-1856 | % | 4.90 | |
Operating Temperature Range | Internal | °C | (-40,+80) | |
Water Absorption % Volume (Maximum) | Internal | % | 0.50 | |
Thermal Conductivity | JIS A1412-2 | W/mK | 0.040 | |
Shore - C | ASTM D2240 | °C | 30 | |
Flammability | FMVSS302 | mm/min | - |
Property
Raw material: LDPE, PE foam+Alu foil
Density: 25~333kg/m3
Length: customized
Wide: 70~1800 mm
Thickness:
xpe 2~3mm 3~12mm
Ixpe 0.1~0.5mm 0.5~3mm, 3~10mm
Color: black,white and gray,other colors can be customized
Shore hardness: 10~80 degree
Reflective:96%~97%
Structure:Closed cell
Surface smooth: Alu
Flammability:B1 grade
Refractoriness:100-150 degree
Thermal Conductivity:0.040~0.095 w/m.k
Water Absorption:(23degree,24h) 0.2~0.6%
Tearing Strength: 0.2~1.8 KN/m
Elongation at break :100%~240%
Tensile Strength: 0.2~1.6 Mpa
Compressed distortion: 2%~10%
Size change rate: -4%`-8%
Thermal conductivity: 0.040 ~0.095 w/m.k
Company info
CYG TEFA is the earliest PE foam manufacturing with scale production in China since 2002.Mainly produce XPE FOAM,IXPE FOAM,IXPP FOAM and ESD PRODUCT(Foam type: PE/EVA/PU/EPE/PP Plastic).Annual production capacity is about 6000 tons.2 bases one in Shen zhen and an other in Huzhou,with total 17 production lines.CYG Management control system: Kingdee / OA / Oracle.CYG have a professional team and technology.More than 30 R&D staff.Through the great variety of our products we provide people with a warm and quiet home and working environment.
11 employee
Investment rate: 4% to 10%
Responsible for : Improving available product / Technology improving / New product development / New devices
IXPP project (three years: Proposal stage - Develop - Sampling - Approved product- Small quantity supply for testing
Contact Person: Cherrie
Tel: +13823739175
Fax: 86-755-26631759